Product descriptions from the supplier
Composite mat is made of two layers.The top layer is fiberglass mesh and the bottom
layer is cotton mat,Through high temperature,stoving,finalizing the design.It is a kind of
reinforcement combination material.
It is characterized as high tensile strength,easy soakage by bitumen,low cost and so on.
1.width: 98cm/99cm/1m or as customers requirement
2.weight:80-110g/m2
3.mesh size:3*3-7*7mm
4.weave type:twill woven
5.yarn type:C-Glass
6.alkali content:medium
7.length of roll:50/100m(the length can loaded more in container and save freight fee)
| Items | Gram Weight
(g/m2) |
Specification | Tensile Strength | Shrinkage
(270°C) |
Elongation(%) | Roll Size
(m x m) |
Quantity
/40’ft |
|
| Vertical(N/5cm) | Cross(N/5cm) | |||||||
| Fiberglass
mat |
80g/m2 | 3X3 | 270 | 240 | <1.0 | 5 | 1.0 x 1400 | 159600m2 |
| 90g/m2 | 4X4 | 320 | 290 | <1.0 | 5 | 1.0 x 1350 | 153900m2 | |
| 110g/m2 | 5X5(I Grade) | 350 | 300 | <1.0 | 5 | 1.0 x 1300 | 148200m2 | |
| 110g/m2 | 5X5(II Grade) | 450 | 400 | <1.0 | 5 | 1.0 x 1300 | 148200m2 | |
| 120g/m2 | 6X6 | 550 | 500 | <1.0 | 5 | 1.0 x 1200 | 136800m2 | |
| 130g/m2 | 7X7 | 660 | 600 | <1.0 | 5 | 1.0 x 1200 | 136800m2 | |
1.Function: It is used for making changed SBS waterproof material, and for waterproof
in the undergorund, building roofing, ground and pond.combination fabric is base cloth
of using SBS waterproof material, its tension of warp and weft is more than 600N.
Among waterproof materials, this kind of product is the best favourable.
2.glass fiber combination non woven is made on the base of non woven by compositing
some density glass fibre, through high temperature, stoving, finalizing the design. It is a
kind of reinforcement combination material.
3.packing:shrank wrapped each roll and put in pallet.
4. Non Stick It can easily remove all kinds of adhesives such as resin, paint and chemical medicine,
easy to clean.
5.Chemical resistance–It can resist all most of chemical medicines.
6.Permeability–It can avoid wasting heat and improve drying efficiency for it’s permeability.